Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin
MFR #:Pedigree® E58
EIS #:PH21-Pedigree E58
MFR #:Pedigree® E58
EIS #:PH21-Pedigree E58
Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin, Epoxy Base Type, Room Temperature Cure Type, 1.1582 g/cm3 (77 °F (25 °C)) Density, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 300 - 400 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
$35.74
- $48.57
Select from the options below
Elantas PDG Pedigree® E58 Two-Component Epoxy Impregnating Resin, Epoxy Base Type, Room Temperature Cure Type, 1.1582 g/cm3 (77 °F (25 °C)) Density, 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water) Dielectric Strength, 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener Flash Point, 5 - 10 min At 25 °C/77 °F Gel Time, 77 Shore D At 25 °C/77 °F Hardness, 100 (Parts By Weight And Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener Mixing Ratio, 300 - 400 CP At 25 °C/77 °F Viscosity, 300 - 400 CP At 25 °C/77 °F Viscosity - Part-A, 40 - 70 CP At 25 °C/77 °F Viscosity - Part-B. - Pedigree® E 58 / C 59M is a two-component, fast curing, epoxy impregnating resin, moisture and chemical-resistant, low viscosity for good penetration.
Product Options
Showing 2 out of 2 options
 | Container Size: 48 lb | EIS Part #: PDGE58PAIL | $ / US pound | |
| Container Size: 532 lb | EIS Part #: E58532LB | $ / US pound |
- Attributes
- Features
- Applications
- Documents
Attributes
General Information
Item NameEpoxy Impregnating Resin
Trade NamePedigree®
SeriesPedigree® E58
General Features
Shelf Life12 Months
TypeTwo-Component
Design & Construction
Base TypeEpoxy
Cure TypeRoom Temperature
FormLiquid
Performance Details
Gel Time5 min
Chemical Properties
Mixing Ratio100 (Parts By Weight and Volume) Resin, 20 (Parts By Weight) 23.3 (Parts By Volume) Hardener
Viscosity300 cP
Viscosity - Part-A300 cP
Viscosity - Part-B40 cP
Electrical Properties
Dielectric Strength1600 V/mil
Physical Properties
Hardness77 Shore D at 25 °C/77 °F
Features
- Rapid cure on room-temperature or preheated units with no oven bake
- High bond strength
- Meter-mix - trickle application method
- Store below 25 °C / 77 °F in a dry controlled environment out of direct sunlight
- Twisted coil bond strength ASTM D4882 over MW 35: 97 pounds at 25 °C / 77 °F, 13 pounds at 150 °C / 302 °F
- 57 °C (DSC) glass transition temperature
- 99 ppm / °C (below Tg), 230 ppm / °C (above Tg) coefficient of thermal expansion
- 0.9% at ASTM D570 - 25 °C / 77 °F water absorption
- 4.3 x 10^13 ohm-cm at ASTM D257 - 25 °C / 77 °F, 3.3 x 10^11 ohm-cm at ASTM D257 - 100 °C / 212 °F volume resistivity
- 4.0 at 1 kHz - 25 °C / 77 °F, 6.6 at 1 kHz - 100 °C / 212 °F dielectric constant
- 0.02 at 1 kHz - 25 °C / 77 °F, 0.27 at 1 kHz - 100 °C / 212 °F dissipation factor
- Secondary insulation
- Dielectric Strength: 1600 V/Mil (ASTM D149 - 9 Mil), 1600 V/Mil (ASTM D149 - 9 Mil After 24 hr in Water)
- Flash Point: 90 °C (ASTM D93) Resin, 171 °C (ASTM D93) Hardener
- Viscosity: 300 - 400 CP at 25 °C/77 °F
- Density: 1.1582 g/cm3 (77 °F (25 °C))
- Viscosity - Part-B: 40 - 70 CP at 25 °C/77 °F
- Gel Time: 5 - 10 min
- Viscosity: 300 - 400 cP
- Viscosity - Part-A: 300 - 400 cP
- Viscosity - Part-B: 40 - 70 cP
Applications
- Impregnation of Motor Armatures and Stators